Description
This product can be used in one of two ways;
- Immerse or swab 1⁄2 –3 min. Add H2O2 dropwise to maintain action.
- Electrolytic at 4 V for 3 to 5 seconds.
E407022
£24.00 – £47.00 Exc VAT
When used as described electrolytically, this product will revel the general structure of high temperature Cobalt Alloys.
For the passivation of Nickel Superalloys, such as UNS Alloy N06625, immerse or swab the specimen as indicated in method 1. Using this product as directed in method 1, is specific for UNS Alloy N10004.
Additional information
| Weight | N/A |
|---|---|
| Dimensions | N/A |
| Container Type | |
| Reagent Type | |
| Method | |
| Indicated Use | For passive alloys, General Structure, UNS Alloy N06625, UNS Alloy N10004 |
| Volume (mls) |
Add a review
You must be logged in to post a review
Log In
Q & A
There are no questions yet
Ask a question
Your question will be answered by a store representative or other customers.
Thank you for the question!
Your question has been received and will be answered soon. Please do not submit the same question again.
Error
An error occurred when saving your question. Please report it to the website administrator. Additional information:
Add an answer
Thank you for the answer!
Your answer has been received and will be published soon. Please do not submit the same answer again.
Error
An error occurred when saving your answer. Please report it to the website administrator. Additional information:
Reviews
There are no reviews yet