Description
This solution will reveal the general structure of pure Nickel and high Nickel alloys, Nickel-Copper alloys and Nickel-Titanium alloys.
It can also be used to reveal the grain boundary sulphidation of Superalloys.
Flat Reagent
£24.00 Exc VAT
Immerse or swab for between 5 to 30 seconds.
This solution will chemically polish with longer times.
Sulphidised grain boundaries will be revealed before normal grain boundaries.
Additional information
| Weight | 0.12 kg |
|---|---|
| Dimensions | 5 × 5 × 11 cm |
| Volume (mls) | |
| Reagent Type | |
| Indicated Use |
Add a review
You must be logged in to post a review
Log In
Q & A
There are no questions yet
Ask a question
Your question will be answered by a store representative or other customers.
This site is protected by reCAPTCHA and the Google Privacy Policy and Terms of Service apply.
Thank you for the question!
Your question has been received and will be answered soon. Please do not submit the same question again.
Error
An error occurred when saving your question. Please report it to the website administrator. Additional information:
Add an answer
This site is protected by reCAPTCHA and the Google Privacy Policy and Terms of Service apply.
Thank you for the answer!
Your answer has been received and will be published soon. Please do not submit the same answer again.
Error
An error occurred when saving your answer. Please report it to the website administrator. Additional information:
Related products
-
Kalling’s Reagent
£26.00 – £64.00 Exc VAT Select options This product has multiple variants. The options may be chosen on the product page -
Barker’s Reagent
£24.00 – £47.00 Exc VAT Select options This product has multiple variants. The options may be chosen on the product page -
Murakami’s Reagent
£27.50 – £78.50 Exc VAT Select options This product has multiple variants. The options may be chosen on the product page -
Klemm’s Reagent
£29.00 – £75.00 Exc VAT Select options This product has multiple variants. The options may be chosen on the product page
Reviews
There are no reviews yet